Astm Paint Adhesion Scratch Test

This test at the simplest level involves the examination of the paint film removed after an applied tape is peeled off.

Astm paint adhesion scratch test.

This procedure can also be administered on site and provides quantitative results in. Other related test methods. On metal substrates a more formal version of the knife test is the tape test. Pressure sensitive tape is applied and removed over cuts made in the coating.

This method assesses the adhesion of either one or multiple coatings on a smooth surface by applying tensile stress rather than shear stress measured in the previous two tests from a dolly to the surface the load is slowly increased until the dolly along with the adhesive layers is removed. Qualtech products industry cross cut adhesion tester cross hatch cutter is a professional instrument engineered to conveniently evaluate the adhesion performance of coatings applied onto specimen. As coatings continue to cure the adhesive properties will change. Normally after 30 days a second test should be performed.

Some coatings will improve in adhesion as the coating continues to cross link other coating systems decrease in adhesion due to different rates of shrinkage between substrate or coating layers within the system. 5 2 the quantitative coating adhesion scratch test is a simple practical and rapid test. 3 4 film adhesion test the coating film adhesion shall be tested in accordance with method b of astm d3359 09e2 standard test methods for measuring adhesion by tape test. One inch wide pressure sensitive.

A standard method for the application and performance of this test is available in astm d6677. Through the patterns and methods of astm d3359 17 s procedures adhesion can be much more easily and reliably measured. There are two variants of this test. Other related tape adhesion test methods include din en iso 2409 paints and varnishes cross cut test fltm bi 106 01 gm 9071p gmw14829 iso 2409 and navistar mpaps gt paint gt 5a.

However reliable and reproducible test results require careful control of the test system configuration and testing parameters detailed analysis of the coating damage features and appropriate characterization of the properties and morphology of the coating and the substrate of the test specimens. Functional behaviour of a coating is critical to its adhesion to the substrate. 1 1 this test method covers the determination of the adhesion of organic coatings such as paint varnish and lacquer when applied to smooth flat planar panel surfaces. This paint adhesion cross cut tester offers a high quality and precision engineered round shaped blade holder presenting selectable blades with 6 or 11 teeth and a.

June 5 2012 4 scratch tests 1. A total of 11 parallel cuts are made with a sharp instrument 1mm apart in both a vertical and horizontal direction forming a grid. 1 2 the values stated in si units are to be regarded as the standard.